Tecnoflon® FKM Ionic Curable 

Tecnoflon® FKM Ionic Curable grades are copolymers and terpolymers with a fluorine content range from 66% to 70% and are well suited for automotive, industrial and aerospace applications. The HS copolymers are designed for low post-cure cycles and cure-incorporated and rubber-to-metal bonding grades are available for all molding techniques.

 
Expand All Collapse All
Typical PropertiesProcessingPerformanceCopolymersTerpolymersData Sheets

Tecnoflon® FKM Ionic Curable grades are proven successful in the following markets:

Raw Copolymers

N 215/U N 535 N 935 N H N 60HS N 90HS
Flourine Content
(weight %)
66 66 66 66 66 66
Specific Gravity (g/cm3)
ASTM D792
1.81 1.81 1.81 1.81 1.81 1.81
Rubber Mooney Visc. ML(1+10) @ 121°C (Units)
ASTM D1646
10 27 62 124 27 45
Tensile Strength (MPa)
ASTM D412C
14.1 17.5 18.5 19.5 15.0 16.1
Elongation at Break (%)
ASTM D412C
186 182 185 175 200 190
Hardness (Shore A)
ASTM 2240
73 74 75 77 68 70
C.Set 70h @200°C on #214 O-Ring (%)
ASTM D395
Method B
18 13 13 12 14 14
TR10 (°C)
ASTM D1329
-17 -17 -17 -17 -17 -17
Post Cure @ 250°C (8+16)h (8+16)h (8+16)h (8+16)h (8+16)h (8+16)h
Notes 1) 1) 1) 2) 2)

1) FDA
2) Curable without CA(OH)2, low post-cure

Cure Incorporated Copolymers

FOR
210
FOR
539
FOR
5351/U
FOR
60K/U
FOR
5312K
Flourine Content
(weight %)
66 66 66 66 66
Specific Gravity (g/cm3)
ASTM D792
1.81 1.81 1.81 1.81 1.81
Rubber Mooney Visc. ML(1+10) @ 121°C (Units)
ASTM D1646
9 21 24 30 41
Tensile Strength (MPa)
ASTM D412C
17.8 16.5 16.2 16.2 17.6
Elongation at Break (%)
ASTM D412C
187 190 249 212 253
Hardness (Shore A)
ASTM 2240
74 76 72 72 74
C.Set 70h @200°C on #214 O-Ring (%)
ASTM D395
Method B
22 18 18 18 18
TR10 (°C)
ASTM D1329
-17 -17 -17 -17 -17
Post Cure @ 250°C (8+16)h (8+16)h (8+16)h (8+16)h (8+16)h
Notes

1) FDA
2) Curable without CA(OH)2, low post-cure

FOR
4353
FOR
7353
FOR
50HS
FOR
80HS
FOR
501HS
FOR
801HS
Flourine Content
(weight %)
66 66 66 66 66 66
Specific Gravity (g/cm3)
ASTM D792
1.81 1.81 1.81 1.81 1.81 1.81
Rubber Mooney Visc. ML(1+10) @ 121°C (Units)
ASTM D1646
20 39 23 38 24 40
Tensile Strength (MPa)
ASTM D412C
15.7 18.2 18.6 18.0 15.0 17.5
Elongation at Break (%)
ASTM D412C
174 174 203 201 270 261
Hardness (Shore A)
ASTM 2240
76 78 70 71 65 65
C.Set 70h @200°C on #214 O-Ring (%)
ASTM D395
Method B
15 16 15 13 17 17
TR10 (°C)
ASTM D1329
-17 -17 -17 -17 -17 -17
Post Cure @ 250°C (8+16)h (8+16)h 1h 1h 1h 1h
Notes 1) 1) 2) 2) 2) 2)

1) FDA
2) Curable without CA(OH)2, low post-cure

Raw Terpolymers

TN 50A TN T 538 T 938
Flourine Content
(weight %)
68 68 68.5 68.5
Specific Gravity (g/cm3)
ASTM D792
1.86 1.86 1.88 1.88
Rubber Mooney Visc. ML(1+10) @ 121°C (Units)
ASTM D1646
23 67 26 66
Tensile Strength (MPa)
ASTM D412C
13.5 17.8 12.1 15.5
Elongation at Break (%)
ASTM D412C
297 230 250 218
Hardness (Shore A)
ASTM 2240
72 77 75 78
C.Set 70h @200°C on #214
O-Ring (%)
ASTM D395
Method B
29 29 31 24
TR10 (°C)
ASTM D1329
-14 -14 -13 -13
Post Cure @ 250°C (8+16)h (8+16)h (8+16)h (8+16)h
Notes 1) 1)

1) FDA

Cure Incorporated Terpolymers

FOR 7380K FOR TF 838K FOR 5381
Flourine Content
(weight %)
68 68 68.5
Specific Gravity (g/cm3)
ASTM D792
1.86 1.86 1.88
Rubber Mooney Visc.
ML(1+10) @ 121°C (Units)
ASTM D1646
32 41 21
Tensile Strength (MPa)
ASTM D412C
16 12.4 15.0
Elongation at Break (%)
ASTM D412C
247 360 200
Hardness (Shore A)
ASTM 2240
75 74 80
C.Set 70h @200°C on #214
O-Ring (%)
ASTM D395
Method B
30 - 23
TR10 (°C)
ASTM D1329
-14 -14 -13
Post Cure @ 250°C (8+16)h (8+16)h (8+16)h
FOR 9385F FOR 9383 FOR 3390
Flourine Content
(weight %)
68.5 68.5 70
Specific Gravity (g/cm3)
ASTM D792
1.88 1.88 1.89
Rubber Mooney Visc.
ML(1+10) @ 121°C (Units)
ASTM D1646
45 60 47
Tensile Strength (MPa)
ASTM D412C
11.5 16.8 14.5
Elongation at Break (%)
ASTM D412C
350 285 240
Hardness (Shore A)
ASTM 2240
75 74 80
C.Set 70h @200°C on #214
O-Ring (%)
ASTM D395
Method B
- 32 32
TR10 (°C)
ASTM D1329
-13 -13 -7
Post Cure @ 250°C (8+16)h (8+16)h (8+16)h

 

Contacts 



Specialty Polymers | Americas
Specialty Polymers Americas

Specialty Polymers | Asia & Australia
Specialty Polymers Asia

Specialty Polymers | Europe, Middle East & Africa
Specialty Polymers EMEA



Literature 





 





 
 
Current Site > SolvayPlastics
 
© SOLVAY 2014 Skip Navigation Links
Last Update (7/8/2014)